Q-switched and mode-locked pulse generation with samarium oxide film saturable absorber

Yusoff, R. A. M. and Jafry, A. A. A. and Kasim, N. and Zulkipli, N. F. and Yasin, M. and Harun, S. W. (2021) Q-switched and mode-locked pulse generation with samarium oxide film saturable absorber. Nonlinear Optics Quantum Optics, 53 (3-4). pp. 323-335. ISSN 1543-0537

Full text not available from this repository.


Q-switched and mode-locked pulses were obtained by utilizing a Samarium oxide (Sm2O3) film as saturable absorber (SA) in Erbium-doped fiber laser (EDFL) cavity. The Sm2O3 SA film has a modulation depth and saturation intensity of 30% and 90 MW/cm2, respectively. The proposed Q-switched EDFL operated stably at 1558.4 nm. The repetition rate was tunable in a range from 75.8 kHz to 99.5 kHz with the raise of pumping power from 81.0 mW to 131.9 mW. At the maximum pumping power of 131.9 mW, the highest pulse energy of 143.9 nJ and the lowest pulse width of 2.12 µs were attained. A stable soliton mode-locked laser was observed at a central wavelength of 1561.6 nm when an additional 100 m long single mode fiber was incorporated into the cavity. The mode-locking operation was maintained at pump power range within 91.2 mW to 142.0 mW with repetition rate of 1.88 MHz and pulse width of 3.40 ps. At 142.0 mW, the maximum pulse energy of 12.00 nJ and peak power of 3.53 kW were obtained. These show that the proposed Sm2O3 SA is viable for application in the construction of practical Q-switched and mode-locked pulses operating in the 1.5 micron range.

Item Type:Article
Uncontrolled Keywords:fiber laser, metal oxide saturable absorber, mode-locking
Subjects:Q Science > QC Physics
ID Code:94731
Deposited By: Narimah Nawil
Deposited On:31 Mar 2022 23:13
Last Modified:31 Mar 2022 23:13

Repository Staff Only: item control page