Fatigue damage of cohesive interfaces in fiber-reinforced polymer composite laminates

Koloor, S. S. R. and Abdullah, M. A. and Tamin, M. N. and Ayatollahi, M. R. (2019) Fatigue damage of cohesive interfaces in fiber-reinforced polymer composite laminates. Composites Science and Technology, 183 . p. 107779. ISSN 0266-3538

Full text not available from this repository.

Official URL: http://dx.doi.org/10.1016/j.compscitech.2019.10777...


The weak interfaces in fiber-reinforced polymer (FRP) composite laminates often dictates the reliability of the composite structures. In this respect, a new cyclic cohesive zone model (CCZM) is introduced for accurate quantitative description of the interlaminar fatigue failure process. The model incorporates the interlaminar damage through the measured fatigue degradation of the strength, stiffness, and critical energy release rate properties. A combined experimental-finite element (FE) approach is employed to establish the residual interlaminar properties. The new CCZM is examined for the case study on the end-notched flexure (ENF) beam specimen of unidirectional carbon fiber-reinforced polymer (CFRP) composite laminate. The calculated applied resultant shear stress at the critical interface material point, adjacent to the pre-existing crack front, fluctuates at (τmax = 30 MPa, R = 0.1). The interlaminar shear-induced damage shows a sigmoidal form of the damage evolution curve. The pre-existing interface crack propagation begins at 301750 cycles, while maintaining an almost straight advancing crack front.

Item Type:Article
Uncontrolled Keywords:Damage mechanics, Finite element analysis (FEA)
Subjects:T Technology > TJ Mechanical engineering and machinery
Divisions:Mechanical Engineering
ID Code:87886
Deposited By: Widya Wahid
Deposited On:30 Nov 2020 21:29
Last Modified:30 Nov 2020 21:29

Repository Staff Only: item control page