Effect of SEBS on the mechanical properties and miscibility of polystyrene rich polystyrene/polypropylene blends

Samsudin, Sani Amril and Hassan, Azman and Mokhtar, Munirah and Syed Jamaluddin, Syed Mustafa (2005) Effect of SEBS on the mechanical properties and miscibility of polystyrene rich polystyrene/polypropylene blends. Progress in Rubber, Plastics and Recycling Technology, 21 (4). pp. 261-276.

PDF (Abstract)


The effects of styrene-b(ethylene-co-butylene)-b-styrene (SEBS) on the mechanical properties and compatibility of PS-rich PS/PP blends were calculated. Blends of PS/PP in various compositions ranging from 100-60 wt percent PS with or without SEBS were prepared and injection moulded using a Brabender PL2000 twin-screw extruder. The impact strength and elongation at break of the PS/PP blends increased with SEBS content, at the expense of tensile strength and flexural modulus. It was observed that the improvements in impact strength and elongation break with addition of SEBS were due to the improved interfacial adhesion between the dispersed phase (PP) and matrix phase (PS). The improvement in miscibility of the PS/PP blend with the addition of SEBS is supported by DMA analysis. This showed that the 60/40 PS/PP blends possess two endothermic peaks whereas 60/40/25 PS/PP/SEBS blends have a single endothermic peak at 102 °C, indicating that they have an improved miscibility. The effectiveness of SEBS in enhancing the blends depends on the blend composition. A significant improvement was observed upon addition of more than 10 phr of SEBS into the 70/30 and 60/40 PS/PP blends, but not much improvement in the case of the 90/10 and 80/20 PS/PP blends. However, a higher SEBS content is more effective at higher PS contents, as illustrated by the 90/10/25 PS/PP/SEBS blends having higher impact strengths than 60/40/25 PS/PP/SEBS. The optimum blend, based on achieving a balance between toughness (impact strength) and stiffness (flexural modulus), is 90/10/25 PS/PP/SEBS, followed by 80/20/25 PS/PP/SEBS.

Item Type:Article
Uncontrolled Keywords:Mechanical properties, miscibility, polystyrene rich polystyrene/polypropylene blends, styrene-b (ethylene-co-butylene)-b-styrene
Subjects:T Technology > T Technology (General)
Divisions:Chemical and Natural Resources Engineering
ID Code:5543
Deposited By: Norhani Jusoh
Deposited On:13 May 2008 04:58
Last Modified:07 Aug 2017 08:23

Repository Staff Only: item control page