Luminescence spectra of TeO ₂-PbO-Li ₂O doped Nd ₂O ₃ glass

Azman, K. and Razali, W. A. W. and Azhan, H. and Sahar, Md. Rahim (2012) Luminescence spectra of TeO ₂-PbO-Li ₂O doped Nd ₂O ₃ glass. In: Advanced Materials Research. Trans Tech Publications, Switzerland, pp. 121-125. ISBN 978-303785402-0

Full text not available from this repository.

Official URL: http://dx.doi.org/10.4028/www.scientific.net/AMR.5...

Abstract

A tellurite glass of TeO 2-PbO-Li 2O doped with Nd 2O 3 has been successfully fabricated by using the conventional melt-quenched technique. The absorption and emission spectroscopy have been identified using UV-VIS-NIR and photoluminescence spectrometer, respectively. From the spectroscopy, ten significant spectra have been observed in the region of 400-900 nm. The absorption wavelength centered at 585 nm attributed to 4I 9/2 → 4G 5/2 transition is the predominant wavelength to be used as the excitation wavelength. Emission spectra have been determined by using 585 nm excitation wavelength at room temperature. From the emission spectra, seven distinctive upconversion bands contributed from Nd 3+ were observed in the region of 400-1500 nm. It was found that the bands were centered at 450 nm ( 4G 11/2 → 4I 9/2), 485 nm ( 4G 11/2 → 4I 11/2), 605 nm ( 4G 11/2 → 4I 15/2), 665 nm ( 4G 7/2 → 4I 13/2), 880 nm ( 4F 3/2 → 4I 9/2), 1062 nm ( 4F 3/2 → 4I 11/2) and 1340 nm ( 4F 3/2 → 4I 11/2), respectively. These emission bands showed the possibility of visible and near infrared emission spectra.

Item Type:Book Section
Additional Information:Indexed by Scopus
Uncontrolled Keywords:absorption, emission, photoluminescence, tellurite glass, upconversion