Optimization of thermoluminescence response of copper doped zinc lithium borate glass co-doped with Na2O

Abstract

Establishing the basic procedures that will influence the enhancement of the TL yield of a phosphor is paramount in the issue of dosimetry. Melt quenching method was adopted in synthesizing lithium borate glass modified with ZnO, doped with CuO and codoped with Na2O. The structural and optical properties of zinc lithium borate and some TL properties of copper doped zinc lithium borate were reported in our previous works. The amorphous nature of the prepared glasses was confirmed by x-ray diffraction analysis (XRD). Physical properties of the glass were obtained via Archimedes principle. The copper doped zinc lithium borate was co-doped with different concentration of Na2O (0.025 mol % to 0.1 mol %). The glasses were irradiated with 4 Gy dose of gamma rays using 60Co gamma cell. The highest TL response was recorded against 0.05 mol% concentration of Na2O. The best settings for TLD reading of the proposed TLD were determined. The optimal annealing temperature and time for this composition was found to be 300 oC and 50 min respectively. The best heating rate at which the new TLD can be readout was 3 oC S-1.