Photocatalytic removal of 2,4-dichlorophenoxyacetic acid herbicide on copper oxide/titanium dioxide prepared by co-precipitation method

Abstract

In this work, suppression of the charge recombination on the titanium dioxide (TiO2) was reported by the addition of copper oxide (CuO), which led to a higher activity of TiO2 for removal of 2,4-dichlorophenoxyacetic acid (2,4-D) herbicide. A series of CuO/TiO2 with CuO loadings of 0.1-1 wt% was prepared through a co-precipitation method. X-ray diffraction patterns revealed that the presence of CuO could not be detected as the low loading amount of CuO might have good dispersion on the surface of TiO2. Diffuse reflectance UV-visible spectra suggested that low loading amount of CuO did not influence the optical property of TiO2. Fluorescence spectroscopy revealed that TiO2 possessed a dominant emission peak of 407 nm at an excitation wavelength of 218 nm. The increasing loading amount of CuO decreased the emission intensity of TiO2, suggesting the successful reduction of charge recombination. After irradiation under UV light for 1 h, CuO(0.1 wt%)/TiO2 gave the highest percentage removal of the herbicide among the samples. The optimum loading amount of CuOmight improve the charge separation and reduce the electron-hole recombination on TiO2 without blocking the active sites, thus leading to the improved photocatalytic activity. This work showed that CuO/TiO2 is a potential photocatalyst for environmental remediation.