Farahany, Saeed and Aghaie-Khafri, M. and Ourdjini, Ali and Idris, Mohd. Hasbullah (2011) Influence of heat treatment on properties of hot isostatically pressed turbine blade superalloy in738. Advanced Materials Research, 264-26 . pp. 502-507. ISSN 1022-6680
Full text not available from this repository.
Official URL: http://dx.doi.org/10.4028/www.scientific.net/AMR.2...
Abstract
Impact of heat treatment on hot isostatically pressed (HIP) Ni-base superalloy has been investigated before and after conducting HIP process. HIP was performed by applying a stress of 120 MPa at a temperature of 1200 °C for 2 hours under argon atmosphere followed by furnace cooling to room temperature. Heat treatment cycle was conducted on the samples according to GEB50A563. Microstructural observation demonstrated the deleterious change of ??? morphology after HIP process which causes to decrease of hardness and creep strength. However, pre heat treatment in compared with cast specimen show slight changes in microstructure but, post heat treatment can revert this change of ??? morphology completely and also increase the mechanical properties.
| Item Type: | Article |
|---|---|
| Uncontrolled Keywords: | heat treatment, Hot Isostatic Pressing (HIP), Superalloy |
| Subjects: | Q Science > QC Physics |
| Divisions: | Mechanical Engineering |
| ID Code: | 44981 |
| Deposited By: | Haliza Zainal |
| Deposited On: | 27 Apr 2015 04:50 |
| Last Modified: | 20 Sep 2017 03:23 |
Repository Staff Only: item control page