Enhanced performance of vertical double gate MOSFET (VDGM) with oblique rotating implantation (ORI) method

Ismail, Razali and I., Saad and M. A., Riyadi and F. M. N., Zul Atfyi and A. M. A., Hamid (2010) Enhanced performance of vertical double gate MOSFET (VDGM) with oblique rotating implantation (ORI) method. In: IEEE International Conference on Semiconductor Electronics, Proceedings, ICSE, 2010, Melaka, Malaysia.

Full text not available from this repository.

Official URL: http://dx.doi.org/10.1109/SMELEC.2010.5549532


An enhanced performance of vertical double gate MOSFET (VDGM) structure was revealed by adopting the oblique rotating ion implantation (ORI) method. The device structure was simulated based on TCAD tools and verified by good matching data with the published experimental results. With ORI method a symmetrical self-aligned source/drain regions over the silicon pillar and sharp vertical channel profile was observed. With Lg = 50nm, the VT is 0.96V in double gate and increased to 1.2V in single gate structure. The sub threshold swing, S = 81.9 mV/dec and S = 87.7 mV/dec were obtained for double and single gate devices respectively. Similarly, large IDsat = 370µA/µm was observed for double gate compared to single gate device. By scaling the Lg into 50nm, the VT remains almost the same when the Lg is larger than 80nm. However, it decreases rapidly when scaled down to 50nm. The leakage current increases rapidly when the Lg is scaled down to 100nm and beyond. However, the ratio of ION - IOFF is seen to be increases even with shorter Lg. These results indicates that ORI method is essential for overcoming various SCE as scaling the channel length down to nanometer regime.

Item Type:Conference or Workshop Item (Paper)
Subjects:T Technology > TK Electrical engineering. Electronics Nuclear engineering
Divisions:Electrical Engineering
ID Code:27116
Deposited By: Mrs Liza Porijo
Deposited On:27 Jul 2012 07:17
Last Modified:05 Feb 2017 08:18

Repository Staff Only: item control page