Idris, Mohd. Hasbullah and Ourdjini, Ali and H., Jafari (2010) High temperature oxidation of AZ91D magnesium alloy granule during in-situ melting. Corrosion Science, 53 (2). pp. 655-663. ISSN 0010-938X
Official URL: http://dx.doi.org/10.1016/j.corsci.2010.10.012
Oxidation behaviour of AZ91D was investigated by heating the alloygranules in a ceramic mould between 650 and 800 °C, for 30 and 60 min. The granules failed to melt in unprotected environment even when the temperature was increased to 800 °C. Raising the temperature increased the oxides thickness linearly, however, oxidation enhanced beyond 750 °C with severe mould–metal reaction and selective oxidation. Heating duration showed more pronounced effect on oxide formation compared to heating temperature. MgO was found to be the dominant compound in oxidation products. Aluminium participated during severe oxidation or combustion to some extent whilst no zinc oxide was detected.
|Uncontrolled Keywords:||a. magnesium, a. alloy, c. oxidation, c. selective oxidation|
|Deposited By:||Liza Porijo|
|Deposited On:||27 Jun 2012 08:28|
|Last Modified:||24 Aug 2014 07:39|
Repository Staff Only: item control page