Characterisation of binary (Nio)(X) (Ag2O)(1_X) nanoparticles synthesised via the thermal treatment route

Absi, Eman and Hamzah, Khaidzir and Ahmad, Nor Ezzaty and Jamaluddin, Khairulnadzmi and Al-Hada, Naif Mohammed and Saleh, Muneer Aziz and Al-Ghaili, Abbas and Shayea, Ibraheem (2023) Characterisation of binary (Nio)(X) (Ag2O)(1_X) nanoparticles synthesised via the thermal treatment route. Ceramics International, 49 (11). pp. 19194-19205. ISSN 0272-8842

Full text not available from this repository.

Official URL: http://dx.doi.org/10.1016/j.ceramint.2023.03.045

Abstract

In this study, binary nickel oxide silver oxide nanoparticles (NiO)x (Ag2O)1-x (NPs) were synthesised for the first time using the thermal treatment route at higher and lower precursor values. Two precursors and 5 g of polyvinyl pyrrolidone (PVP) were employed to obtain the (NiO)x (Ag2O)1-x NPs at 700 °C. The obtained NiO NPs documented cubic and hexagonal phases when assessed with X-ray diffraction (XRD) at (x = 0.4 and 0.6) and (x = 0.2 and 0.8), respectively. The cubic phase was confirmed for Ag2O NPs in all prepared samples. The smallest crystallite and particle sizes were found at x = 0.8. The particle size ranged from 23.0 to 45.0 nm, which was evaluated with a transmission electron microscope (TEM). Two shapes, NiO doped with porous Ag2O nanosheets, were observed with a scanning electron microscope (SEM). The purity of the products was evaluated via energy-dispersive X-ray (EDX) spectroscopy. The synthesised NPs were composed of nickel (Ni), silver (Ag), and oxygen (O). Moreover, the X-ray photoelectron spectroscopy (XPS) analysis performed during this study revealed the chemical states of the Ni, Ag, and O present, which confirmed the purity of the NPs. The ultraviolet–visible spectroscopy (UV–Vis) assessment conducted also demonstrated that the energy band gaps for nickel oxide (NiO) and silver oxide (Ag2O) increased with rising x values. The photoluminescence (PL) analysis performed in this study also verified the existence of two emission peaks attributable to NiO and Ag2O, indicating that the NPs possess good photocatalytic activity. Consequently, the NPs synthesised in the present study could be applied as antimicrobial agents in wastewater treatment.

Item Type:Article
Uncontrolled Keywords:Binary oxide (NiO)x (Ag2O)1-x NPs, Metal oxide nanoparticles, Polyvinyl pyrrolidone, Structural properties, Thermal treatment method
Subjects:T Technology > TP Chemical technology
Divisions:Chemical and Energy Engineering
ID Code:105861
Deposited By: Widya Wahid
Deposited On:20 May 2024 07:18
Last Modified:20 May 2024 07:18

Repository Staff Only: item control page