Mechanical properties of PALF/Kevlar-reinforced unsaturated polyester hybrid composite laminates

Abstract

Natural and synthetic fibres are in high demand due to their superior properties. Natural fibres are less expensive and lighter as compared to synthetic fibres. Synthetic fibres have drawn much attention, especially for their outstanding properties, such as durability, and stability. The hybridisation between natural and synthetic fibres composite are considered as an alternative to improve the current properties of natural and synthetic fibres. Therefore, this study aimed to determine the physical and mechanical properties of pineapple leaf fibre (PALF) and Kevlar reinforced unsaturated polyester (UP) hybrid composites. The PALF/Kevlar hybrid composites were fabricated by using hand layup method utilising unsaturated polyester as the matrix. These composites were laid up to various laminated configurations, such as [PKP]s, [PPK]s, [KPP]s, [KKP]s, [PPP]s and [KKK]s, whereby PALF denoted as P and Kevlar denoted as K. Next, they were cut into size and dimensions according to standards. Initially, the density of PALF/Kevlar reinforced unsaturated polyester were evaluated. The highest density result was obtained from [KKK]s, however, the density of hybrid composites was closely indistinguishable. Next, moisture absorption behaviour and its effects on the PALF/Kevlar reinforced unsaturated polyester were investigated. The water absorption studies showed that the hybridisation between all PALF and Kevlar specimens absorbed moisture drastically at the beginning of the moisture absorption test and the percentage of moisture uptake increased with the volume fraction of PALF in the samples. The tensile test indicated that all specimens exhibited nonlinear stress-strain behaviour and shown a pseudo-ductility behaviour. [KKP]s and [KPK]s hybrid composites showed the highest tensile strength and modulus. The flexural test showed that [KPK]s had the highest flexural strength of 164.0 MPa and [KKP]s had the highest flexural modulus of 12.6 GPa. In terms of the impact strength and resistance, [KKP]s outperformed the composite laminates. According to SEM scans, the hybrid composites demonstrated a stronger interfacial adhesion between the fibres and matrix than pure PALF composite.