Fabrication and evaluation of nanofiltration membrane coated with amino-functionalized graphene oxide for highly efficient heavy metal removal

Abstract

In this study, two different methods were used to introduce functionalized graphene oxide (GO) onto the surface of nanofiltration (NF) membrane to improve its performance for heavy metal removal. The first method was based on coating in which the surface of NF membrane was coated with cross-linked GO, while the second method was introducing GO into monomer solution during interfacial polymerization. The efficiency of different methods was then compared by characterizing membrane physiochemical properties, as well as separation performance. With regard to performances, the water flux of TFN-i2 membrane (with GOs incorporated into thin layer) was reported to be 95 L/m2 h compared to 75 L/m2 h found in the TFN-c2 membrane (with GOs coated on the surface) at 8 bar. Both modified membranes exhibited higher water flux than the control membrane without GO incorporation (40 L/m2 h). Although the water flux of TFN-c2 membrane was lower, it achieved higher cobalt removal (97%) than that of TFN-i2 membrane (73%) due to its higher negative surface charge that improved separation via the Donnan exclusion effect.