Shamsudin, Zuraidy (2007) Developement of ceramic cutting insert of alumina (Al2O3) and zirconia / zirconium oxide (ZrO2) for turning tool steel. Masters thesis, Universiti Teknologi Malaysia, Faculty of Mechanical Engineering.
Restricted to Repository staff only
PDF (Table Of Content)
PDF (1st Chapter)
The production of cutting tool insert using a powder technology is a process that is widely use today especially for ceramic cutting tool. The powder technology that has been use involve three phases which is, firstly the raw material will be grind to nanometer size powder. In second phase, the powder will be compacted using special mold with high pressure, and after that sintering process will take place for the third phase. In this study, two nanometer size ceramic powders will be mixed together with a suitable composition to produce a better final product. This production concept is similarly with the production of ‘ceramic matrix composite’ material which is the reinforce material will be added to the ceramic base material or ceramic matrix. There are several sintering process that can be use for this study, for example, normal sintering process, and hot isocratic process with high pressure furnace.
|Item Type:||Thesis (Masters)|
|Additional Information:||Thesis (Sarjana Kejuruteraan (Mekanikal - Teknologi Pembuatan Termaju)) - Universiti Teknologi Malaysia, 2007; Supervisor : Assoc. Prof. Dr. Safian Sharif|
|Uncontrolled Keywords:||cutting tool insert, powder technology, ceramic cutting tool, turning tool steel|
|Subjects:||T Technology > TJ Mechanical engineering and machinery|
T Technology > TS Manufactures
|Deposited By:||Ms Zalinda Shuratman|
|Deposited On:||30 Jul 2010 02:00|
|Last Modified:||18 Sep 2012 03:35|
Repository Staff Only: item control page